ねじり押出しによるMg 合金AZ 31の結晶粒微細化-分析電子顕微鏡システム利用研究成果、そのXXI(3) - |
|
言語 |
ja |
| タイトル |
|
|
タイトル |
Grain refinement behavior of magnesium alloy AZ31 under torsion extrusion -Research works accomplished by using Electron Microscope System : XXI(3)- |
|
言語 |
en |
| 言語 |
|
|
言語 |
jpn |
| キーワード |
|
|
言語 |
en |
|
主題Scheme |
Other |
|
主題 |
torsion extrusion |
| キーワード |
|
|
言語 |
en |
|
主題Scheme |
Other |
|
主題 |
large strain process |
| キーワード |
|
|
言語 |
en |
|
主題Scheme |
Other |
|
主題 |
magnesium alloy |
| キーワード |
|
|
言語 |
en |
|
主題Scheme |
Other |
|
主題 |
very fine grain |
| キーワード |
|
|
言語 |
en |
|
主題Scheme |
Other |
|
主題 |
pole figure |
| 資源タイプ |
|
|
資源タイプ識別子 |
http://purl.org/coar/resource_type/c_6501 |
|
資源タイプ |
departmental bulletin paper |
| ID登録 |
|
|
ID登録 |
10.34411/00001065 |
|
ID登録タイプ |
JaLC |
| 著者 |
竹内, 敏幸
西原, 佳彦
三井, 和博
奥村, 秀人
水沼, 晋
Takeuchi, Toshiyuki
Nishihara, Yoshihiko
Mitsui, Kazuhiro
Okumura, Hidehito
Mizunuma, Susumu
|
| 抄録 |
|
|
内容記述タイプ |
Abstract |
|
内容記述 |
Magnesium alloy AZ3 l was used to investigate the influence of temperature and speed ratio (= die rotation speed / extrusion speed) on the grain refinement behavior and crystal orientation in torsion extrusion using circular type dies with differemt outlet-hole diameters. For each die, the optimum temperature and the speed ratio required to obtain a uniform distribution of 卜2μmfine grains over the entire cross section of the specimen were clarified. The torsion-extruded specimen had a very different crystal orientation than that of the extruded specimen. At a temperature of 443 K, the torsion-extruded specimen tended to form a strong <0001> texture along the extrusion axis, especially in the center region of the cross section. In contrast, the conventional extrusion sample had many grains in the <0001> direction perpendicular to the extrusion axis. When the outlet-hole diameter was the largest, the torsion-extruded specimen exhibited a strong <0001> texture along the extrusion axis over a wide area of the cross section. In conclusion, both the grain size and the texture of the metals could be controlled over a wide range by changing the die-hole diameter and the speed ratio in torsion extrusion. |
|
言語 |
en |
| 書誌情報 |
神奈川工科大学研究報告.B,理工学編
巻 35,
p. 31-36,
発行日 2011-03-20
|
| 出版者 |
|
|
出版者 |
神奈川工科大学 |
| ISSN |
|
|
収録物識別子タイプ |
PISSN |
|
収録物識別子 |
09161902 |
| 書誌レコードID |
|
|
収録物識別子タイプ |
NCID |
|
収録物識別子 |
AA12669200 |
| フォーマット |
|
|
内容記述タイプ |
Other |
|
内容記述 |
application/pdf |
| 著者版フラグ |
|
|
出版タイプ |
VoR |
|
出版タイプResource |
http://purl.org/coar/version/c_970fb48d4fbd8a85 |
kkb-035-006.pdf (2.8 MB)